Product Name	Seamless Oil Pipe
Material	GR.B,ST52, ST35, ST42, ST45,X42, X46, X52, X56, X60, X65, X70,SS304, SS316 etc.
Size	Size 1/4" to 24" Outside Diameter 13.7 mm to 610 mm
Standard	API5L , ASTM A106 Gr.B, ASTM A53 Gr.B,ANSI A210-1996, ANSI B36.10M-2004,ASTM A1020-2002, ASTM A179-1990,BS 3059-2,DIN 17175 ,DIN 1630 ,DIN 2448
Certificates	API5L, ISO 9001:2008,SGS, BV,CCIC
Wall thickness	SCH10, SCH20, SCH30, STD, SCH40, SCH60, SCH80, SCH100 SCH120, SCH160, XS, XXS
Surface Treatment	black paint, varnish, oil, galvanized, anti corrosion coatings
Marking	Standard marking, or according to your request. Marking Method: Spray white paint
Pipe Ends	Under 2 inch plain end. 2 inch and above Beveled. Plastic caps (small OD) ,Iron protector (large OD)
Pipe Length	1. Single Random Length and double Random Length. 2. SRL:3M-5.8M DRL:10-11.8M or As clients requested length 3. fixed length(5.8m, 6m, 12m)
Packaging	Loose package; Packaged in bundles(2Ton Max); bundled pipes with two slings at the both end for easy loading and discharging; End with Plastic caps; wooden cases.
Test	Chemical Component Analysis, Mechanical Properties, Technical Properties, Exterior Size Inspection, hydraulic testing , X-ray Test.
Application	oil pipe; gas pipe
Advantages	1.Reasonable price with excellent quality 2.Abundant stock and prompt delivery 3.Rich supply and export experience, sincere service 4.Reliable forwarder, 2-hour away from port.

PRODUCT	GRADE	DIAMETER	END TYPE
Q125 TUBING	J55, JFBNAU, L80, P110, 1% Chrome	2.375" – 3.5"	Plain End EUE 8RD
Q125 CASING	J-55, L80 HC, P110 HC	4.5" – 9.625" (J55, L80 HC, P110 HC) 10.75” - 20” (J55)	Plain End, STC, LTC, BTC

API 5CT Q125 Casing serves to transport both crude oil and natural gas from oil and gas layer to the surface pipeline after
drilling is completed. It is able to bear the pressure produced by the exploitation process. After the outer surface is coated
with a protective layer, the tubing is marked in accordance with the API 5CT standard and strapped with metal belt.

API 5CT Q125 Casing can be widely applicable to petroleum, construction, shipbuilding, smelting, aviation, electric power,
food, paper, chemical industry, medical equipment, boilers, heat exchangers, metallurgy and so on.

Technical data

Chemical Composition

Group	Grade	Type	C		Mn		Mo		Cr		Ni max.	Cu max.	P max.	S max.	Si max.
Group	Grade	Type	min.	max.	min.	max.	min.	max.	min.	max.	Ni max.	Cu max.	P max.	S max.	Si max.
1	2	3	4	5	6	7	8	9	10	11	12	13	14	15	16
1	H40	-	-	-	-	-	-	-	-	-	-	-	0.03	0.03	-
	J55	-	-	-	-	-	-	-	-	-	-	-	0.03	0.03	-
	K55	-	-	-	-	-	-	-	-	-	-	-	0.03	0.03	-
	N80	1	-	-	-	-	-	-	-	-	-	-	0.03	0.03	-
	N80	Q	-	-	-	-	-	-	-	-	-	-	0.03	0.03	-
	R95	-	-	0.45 c	-	1.9	-	-	-	-	-	-	0.03	0.03	0.45
2	M65	-	-	-	-	-	-	-	-	-	-	-	0.03	0.03	-
	L80	1	-	0.43 a	-	1.9	-	-	-	-	0.25	0.35	0.03	0.03	0.45
	L80	9Cr	-	0.15	0.3	0.6	0.9	1.1	8	10	0.5	0.25	0.02	0.01	1
	L80	13Cr	0.15	0.22	0.25	1	-	-	12	14	0.5	0.25	0.02	0.01	1
	C90	1	-	0.35	-	1.2	0.25 b	0.85	-	1.5	0.99	-	0.02	0.01	-
	T95	1	-	0.35	-	1.2	0.25 d	0.85	0.4	1.5	0.99	-	0.02	0.01	-
	C110	-	-	0.35	-	1.2	0.25	1	0.4	1.5	0.99	-	0.02	0.005	-
3	P110	e	-	-	-	-	-	-	-	-	-	-	0.030 e	0.030 e	-
4	Q125	1	-	0.35		1.35	-	0.85	-	1.5	0.99	-	0.02	0.01	-

a The carbon content for L80 may be increased up to 0.50 % maximum if the product is oil-quenched.
b The molybdenum content for Grade C90 Type 1 has no minimum tolerance if the wall thickness is less than 17.78 mm.
c The carbon content for R95 may be increased up to 0.55 % maximum if the product is oil-quenched.
d The molybdenum content for T95 Type 1 may be decreased to 0.15 % minimum if the wall thickness is less than 17.78 mm.
e For EW Grade P110, the phosphorus content shall be 0.020 % maximum and the sulfur content 0.010 % maximum.
NL = no limit. Elements shown shall be reported in product analysis.

Tensile and hardness requirements

Group	Grade	Type	Total elongation under load %	Yield strength MPa		Tensile strength min. MPa	Hardness a max.		Specified wall thickness mm	Allowable hardness variation b HRC
Group	Grade	Type	Total elongation under load %	min.	max .		HRC	HBW	Specified wall thickness mm	Allowable hardness variation b HRC
1	2	3	4	5	6	7	8	9	10	11
1	H40	-	0.5	276	552	414	-	-	-	-
	J55	-	0.5	379	552	517	-	-	-	-
	K55	-	0.5	379	552	655	-	-	-	-
	N80	1	0.5	552	758	689	-	-	-	-
	N80	Q	0.5	552	758	689	-	-	-	-
	R95	-	0.5	655	758	724	-	-	-	-
2	M65	-	0.5	448	586	586	22	235	-	-
	L80	1	0.5	552	655	655	23	241	-	-
	L80	9Cr	0.5	552	655	655	23	241	-	-
	L80	13Cr	0.5	552	655	655	23	241	-	-
	C90	1	0.5	621	724	689	25.4	255	≤ 12.70 12.71 to 19.04 19.05 to 25.39 ≥ 25.40	3.0 4.0 5.0 6.0
	T95	1	0.5	655	758	724	25.4	255	≤ 12.70 12.71 to 19.04 19.05 to 25.39 ≥ 25.40	3.0 4.0 5.0 6.0
	C110	-	0.7	758	828	793	30	286	≤ 12.70 12.71 to 19.04 19.05 to 25.39. ≥ 25.40	3.0 4.0 5.0 6.0
3	P110	-	0.6	758	965	862	-	-	-	-
4	Q125	1	0.65	862	1034	931	b	-	≤ 12.70 12.71 to 19.04 ≥ 19.05	3.0 4.0 5.0

a In case of dispute, laboratory Rockwell C hardness testing shall be used as the referee method.
b No hardness limits are specified, but the maximum variation is restricted as a manufacturing control in accordance with 7.8 and 7.9 of API Spec. 5CT.

CUSTOMER TRANSACTION

Always adhere to the tenet of high quality, low cost, fast pace and excellent service. Shandong Chengshun Metal Materials Co., Ltd. is willing to cooperate sincerely with friends from all walks of life at home and abroad for common development.

STORAGE VIDEO

Factory Appearance

Shandong Chengshun Metal Materials Co., Ltd. is located in Jinan City, Shandong Province. It is a comprehensive company dealing in high-quality steel products, with a superior geographical location and very convenient transportation. The company has a complete and scientific quality system, and has been recognized by the industry for its integrity, strength and product quality.

CERTIFICATE OF HONOR

COOPERATIVE PARTNER

PRODUCTION WORKSHOP

Seamless Steel Pipe